Excellent extruded Processing Uncured Fluoroelatomer FKM Precompound For Oil Hose And Fuel Rope
Material Type: FKM A( copolymer) , FKM B( terpolymer), FKM GF grade Fluoroelastomer precompound.
Temperature range: -20 to 250 degree
Processing Method: Extrusion.
Compound Color: Black, brown, red, green and other colors
Material Hardness: 50 to 90 Shore A
Appearance: Solid light yellow or milk rubber block
End products: Fuel hose, FKM tube, Fluorine cord, FPM rope and other irregular shape extruded products
Fluoroelastomer work well in:
ASTM-Reference Fuel C
ASTM-Reference Fuel D
ASTM-Reference Oil No.1
ASTM-Reference Oil No.3
Except oil and acid resistance Fluoroelastomer FKM FKM also have good heat resistance/ozone resistance/weather resistance/water resistance/good machinability.
Application: FKM material is widely used as sealing parts in Modern aviation, missile, rocket, semiconductor, automobile, petroleum, chemical, machinery and other industrial fields.
Typical Property Data sheet:
| Grade | Polymer properties | Mechanical Properties | Description / Features | Typical Uses |
| Viscosity | Color | Gravity | Fluorine Content | TR10 | Tensile | Elongation | Hardness | Compression Set |
| ML(1+10)@121℃ | | g/cm3 | % | ℃ | Mpa | % | Shore A | ASTM D395 Method B(70hrs@200C) |
| Oil Hose/Extruded Hose Application Precompounds |
| FT30P | 32 | White | 1.86 | 68 | -13 | 13.5 | 270 | 75 | 34 | Excellent flowability and extrudability,good mold release | Extruded hoses /profiles |
| FC25P | 25 | White | 1.82 | 66 | -17 | 13 | 220 | 77 | 20 | Good property in rolling,improved extrudability | Extrusion of hoses and profiles |
PROPERTY TEST REPORT/物性测试报告 | Report No/报表编号: | S50 |
| Customer/客户名称: | | Test Date/测试日期 | |
| Product/产品名称: | | Material/主体材料: | FKM precompound |
| Expiration date /保质期: | 24 moths | Formulation No./配方编号: | |
| Our Ref/生产批号: | | Colour/颜色: | White or light yellow |
| Press Cure/一段硫化 | 160℃*45min | Post Cure/二段硫化: | No post cure |
| Room Temperature/温度 | 23 | Humidity/湿度: | 55% |
| Spec: ASTM |
Test Item
测试项目 | G558 | QFB-30P | Test Method
测试标准 |
| 门尼粘度:Mooney Viscosity,ML1+10@121℃ | 28 | 30 | ASTM D1646 |
| Curing items 硫化条件: Test temperature :160℃ Test Time :45min |
| (TS2)Scorch time,Ts2,sec | 6:05 | 3:23 | ASTM D1646 |
| (TC10)Scorch time,Tc10,sec | 5:32 | 3:18 | ASTM D1646 |
| (TC90)Time to 90%cure,t'90,sec | 12:41 | 15:24 | ASTM D1646 |
| (ML)Minimum torque,ML,lbf-in | 0.97 | 1.43 | ASTM D1646 |
| (MH)Minimum torque,MH,lbf-in | 15.38 | 17.45 | ASTM D1646 |
| Typical Properties Test/常规物性测试: |
| 硬度:Hardness Shore A | 77 | 72 | ASTM D2240 |
| 拉伸强度:Tensile strength(MPa) | 11.5 | 11.9 | ASTM D412,Die C |
| 扯断伸长率:Elongation(%) | 353 | 338 | ASTM D412,Die C |
| 压缩永久变形:Compression Set | / | / | |
| 标准配方 Standard Formula | Fluoroelastomer:100 phr MgO(Active 150):3 phr Ca(OH)2:6 phr Carbon black N774:13 phr |